Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 wm material at 600 °C and a load of 250 N The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data w... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 260 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 wm material at 600 °C and a load of 250 N (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 280 N The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data w... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 217 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 189 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_cg material at 600 °C and a load of 189 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 250 N (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 3 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 217 N (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 240 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 240 N (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 250 N (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 250 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 280 N (third repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 240 N (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_cg material at 600 °C and a load of 217 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_cg material at 600 °C and a load of 250 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 250 N The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data w... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 217 N (second repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 240 N (second repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN