Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Uniaxial creep test data for P91 material at 600 °C and a stress of 145 MPa The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Uniaxial creep test data for P91 material at 600 °C and a stress of 160 MPa The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Uniaxial creep test data for P91 material at 600 °C and a stress of 135 MPa (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Uniaxial creep test data for P91 material at 600 °C and a stress of 145 MPa (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Uniaxial creep test data for P91 wm material at 600 °C and a stress of 145 MPa The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Uniaxial creep test data for P91 wm material at 600 °C and a stress of 179 MPa The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Uniaxial creep test data for P91 material at 600 °C and a stress of 155 MPa The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 217 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 189 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 250 N (second repeat test) The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data w... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 240 N (third repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at 22 °C and a displacement rate of .0055 mm/s (second repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -158 °C and a displacement rate of .0055 mm/s (repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at 22 °C and a displacement rate of .0055 mm/s (repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -158 °C and a displacement rate of .0055 mm/s Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -196 °C and a displacement rate of .0055 mm/s Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -60 °C and a displacement rate of .0055 mm/s Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at 22 °C and a displacement rate of .0055 mm/s Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -158 °C and a displacement rate of .0055 mm/s (second repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -158 °C and a displacement rate of .0055 mm/s (third repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN