Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -10 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -150 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -192 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -158 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at 23 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -192 °C and a displacement rate of .003 mm/s (third repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -158 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -120 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -100 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -60 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 wm material at -100 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 wm material at 23 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -135 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 wm material at -192 °C and a displacement rate of .003 mm/s (second repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 wm material at -192 °C and a displacement rate of .003 mm/s (third repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 wm material at -158 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 wm material at -192 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 wm material at -158 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 wm material at -192 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN