Last updated: 19 Dec 2018 | Recent visits: 0 O DIN-PE-OPEN-9101 Test data for uniaxial tensile on material AISI 316 L - sj at 425 Celsius Tensile test data produced in the context of fusion research on the ductility of irradiated 316 welds. Electron beam and shielded metal arc weld joints in solution annealed 316 L plate were sampled along their heat affected zone and molten zone. The samples ... WEB DWN
Last updated: 19 Dec 2018 | Recent visits: 0 O DIN-PE-OPEN-9101 Test data for uniaxial tensile on material AISI 316 L - sj at 425 Celsius Tensile test data produced in the context of fusion research on the ductility of irradiated 316 welds. Electron beam and shielded metal arc weld joints in solution annealed 316 L plate were sampled along their heat affected zone and molten zone. The samples ... WEB DWN
Last updated: 19 Dec 2018 | Recent visits: 0 O DIN-PE-OPEN-9101 Test data for uniaxial tensile on material AISI 316 L - sj at 425 Celsius Tensile test data produced in the context of fusion research on the ductility of irradiated 316 welds. Electron beam and shielded metal arc weld joints in solution annealed 316 L plate were sampled along their heat affected zone and molten zone. The samples ... WEB DWN
Last updated: 19 Dec 2018 | Recent visits: 0 O DIN-PE-OPEN-9101 Test data for uniaxial tensile on material AISI 316 L - sj at 395 Celsius Tensile test data produced in the context of fusion research on the ductility of irradiated 316 welds. Electron beam and shielded metal arc weld joints in solution annealed 316 L plate were sampled along their heat affected zone and molten zone. The samples ... WEB DWN
Last updated: 19 Dec 2018 | Recent visits: 0 O DIN-PE-OPEN-9101 Test data for uniaxial tensile on material AISI 316 L - sj at 395 Celsius Tensile test data produced in the context of fusion research on the ductility of irradiated 316 welds. Electron beam and shielded metal arc weld joints in solution annealed 316 L plate were sampled along their heat affected zone and molten zone. The samples ... WEB DWN
Last updated: 19 Dec 2018 | Recent visits: 0 O DIN-PE-OPEN-9101 Test data for uniaxial tensile on material AISI 316 L - sj at 360 Celsius Tensile test data produced in the context of fusion research on the ductility of irradiated 316 welds. Electron beam and shielded metal arc weld joints in solution annealed 316 L plate were sampled along their heat affected zone and molten zone. The samples ... WEB DWN
Last updated: 19 Dec 2018 | Recent visits: 0 O DIN-PE-OPEN-9101 Test data for uniaxial tensile on material AISI 316 L - sj at 360 Celsius Tensile test data produced in the context of fusion research on the ductility of irradiated 316 welds. Electron beam and shielded metal arc weld joints in solution annealed 316 L plate were sampled along their heat affected zone and molten zone. The samples ... WEB DWN
Last updated: 19 Dec 2018 | Recent visits: 0 O DIN-PE-OPEN-9101 Test data for uniaxial tensile on material AISI 316 L - sj at 360 Celsius Tensile test data produced in the context of fusion research on the ductility of irradiated 316 welds. Electron beam and shielded metal arc weld joints in solution annealed 316 L plate were sampled along their heat affected zone and molten zone. The samples ... WEB DWN
Last updated: 19 Dec 2018 | Recent visits: 0 O DIN-PE-OPEN-9101 Test data for uniaxial tensile on material AISI 316 L - sj at 360 Celsius Tensile test data produced in the context of fusion research on the ductility of irradiated 316 welds. Electron beam and shielded metal arc weld joints in solution annealed 316 L plate were sampled along their heat affected zone and molten zone. The samples ... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -130 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -100 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -30 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -60 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -70 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -10 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at 21 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -192 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -130 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -30 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN