Last updated: 6 Feb 2019 | Recent visits: 0 O DIN-PE-NESC-IV Uniaxial tensile test data for A533B wm material at -50 °C The Network for Evaluating Structural Components (NESC) coordinated extensive materials testing and fracture analyses performed by a group of twenty European organizations. The NESC-IV project addressed the transferability of fracture toughness data from labor... WEB DWN
Last updated: 6 Feb 2019 | Recent visits: 0 O DIN-PE-NESC-IV Uniaxial tensile test data for A533B wm material at -70 °C The Network for Evaluating Structural Components (NESC) coordinated extensive materials testing and fracture analyses performed by a group of twenty European organizations. The NESC-IV project addressed the transferability of fracture toughness data from labor... WEB DWN
Last updated: 6 Feb 2019 | Recent visits: 0 O DIN-PE-NESC-IV Impact test data for A533B wm material at -25 °C and a notch impact energy of 54 J The Network for Evaluating Structural Components (NESC) coordinated extensive materials testing and fracture analyses performed by a group of twenty European organizations. The NESC-IV project addressed the transferability of fracture toughness data from labor... WEB DWN
Last updated: 6 Feb 2019 | Recent visits: 0 O DIN-PE-NESC-IV Impact test data for A533B wm material at -2 °C and a notch impact energy of 75 J The Network for Evaluating Structural Components (NESC) coordinated extensive materials testing and fracture analyses performed by a group of twenty European organizations. The NESC-IV project addressed the transferability of fracture toughness data from labor... WEB DWN
Last updated: 6 Feb 2019 | Recent visits: 0 O DIN-PE-NESC-IV Impact test data for A533B wm material at 22 °C and a notch impact energy of 114 J The Network for Evaluating Structural Components (NESC) coordinated extensive materials testing and fracture analyses performed by a group of twenty European organizations. The NESC-IV project addressed the transferability of fracture toughness data from labor... WEB DWN
Last updated: 6 Feb 2019 | Recent visits: 0 O DIN-PE-NESC-IV Impact test data for A533B wm material at -50 °C and a notch impact energy of 29 J The Network for Evaluating Structural Components (NESC) coordinated extensive materials testing and fracture analyses performed by a group of twenty European organizations. The NESC-IV project addressed the transferability of fracture toughness data from labor... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -10 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -30 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -60 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -100 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -120 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -135 °C and a displacement rate of .003 mm/s The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -158 °C and a displacement rate of .003 mm/s (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -192 °C and a displacement rate of .003 mm/s (second repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -192 °C and a displacement rate of .003 mm/s (third repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 250 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 217 N (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 217 N (second repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 0 O DIN-PTT-INTEGRITY Small punch creep test data for P91 haz_fg material at 600 °C and a load of 240 N (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN