Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 279 N (second repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 284 N (second repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 294 N (third repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 284 N (repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 264 N Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 245 N Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 305 N Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 1 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 279 N (third repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 264 N (repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 280 N (repeat test) The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data w... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -192 °C and a displacement rate of .003 mm/s (second repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 wm material at 600 °C and a load of 217 N The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data w... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -168 °C and a displacement rate of .0055 mm/s Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch tensile/fracture test data for P91 material at -158 °C and a displacement rate of .0055 mm/s (tenth repeat test) Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP5 Growth Project (GRD 1/10886. 2005.), the data for which ar... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Uniaxial creep test data for P91 material at 600 °C and a stress of 155 MPa (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 280 N (second repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 wm material at 600 °C and a load of 240 N The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data w... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 wm material at 600 °C and a load of 250 N The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data w... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 material at 600 °C and a load of 260 N The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN
Last updated: 2 Aug 2018 | Recent visits: 2 O DIN-PTT-INTEGRITY Small punch creep test data for P91 wm material at 600 °C and a load of 250 N (repeat test) The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation o... WEB DWN